This article explains common condition issues found in bronze, brass, and other metal objects to help you determine if these condition issues are present in your metal objects.
This article contains the following sections:
Handling Metal Objects
Handle metal objects with clean, dry hands and remove rings or dangling bracelets. Never place pressure on small parts or applied decorative handles when picking up these objects. If the piece has a lid or other unsecured parts, remove them before handling the item. To examine the bottom or underside, you may want to lay the object on its side on a soft surface, such as a loosely rolled towel.
Metal Object Condition Issues
Please keep in mind that discovering condition issues will not necessarily hurt the sales value of your item. However, listing those issues in your Item Description will decrease the likelihood of buyer complaints and improve the bidder experience. Additionally, some condition issues are inherent to the materials used and their presence can confirm the age of the object.
Once you’ve set up the metal object for examination, you should look for the following issues:
- Dents or Bends
- Scratches and Gouges
- Pitting
- Losses
- Damage to Patina
- Chips or Losses to Base
- Repairs
- Wear to Gilding
Dents or Bends
Carefully examine the surface of the work from all angles. Run your fingertips over the surface. Do you notice any depressions, indentations, or dents? Can you determine if the object has been bent or dropped?
Scratches and Gouges
Carefully examine the object. Do not forget the underside and areas near the base. Are there any light scratches to the surface? Scratches can result from normal use or overzealous cleaning. Are there any gouges, or deeper scratches?
Pitting
Pitting can manifest as small cavities, pinpoints, or depressions, or as a pattern of etching. Pitting is caused by weathering, erosion, and other corrosive processes.
Losses
Are there any broken or missing components? Carefully examine detailed areas and applied decoration. Make note of missing handles, finials, or lids.
Damage to Patina
The term patina refers to the surface appearance of metals. Patina can develop naturally over time or may be deliberately applied by the artist or maker. Carefully assess the condition of a patinated surface. Are there areas of wear, loss, or discoloration? Make note of irregular patterns of corrosion.
Chips or Losses to Base
A base, plinth, pedestal, or stand is often employed to support a sculptural work. Closely examine the base. Are there any chips, cracks, or losses? Has the base been broken and repaired? Is the work firmly attached to the base?
Repairs
Run your fingers over the object. Do you notice any inconsistencies in the surface? Examine the applied decoration and handles, if present. Is there any evidence of repair or re-soldering?
Wear to Gilding
A gilded item is covered in a thin application of gold or silver that is different from the base material. This surface application is delicate and can show signs of wear. Check for losses.